[en] OBJECTIVES: Mismatch in thermal expansion coefficient between core and veneering ceramic (Deltaalpha=alphacore-alphaveneer, ppm/ degrees C) is reported as a crucial parameter influencing veneer fractures with Yttria-tetragonal-zirconia-polycrystal (Y-TZP) prostheses, which still constitutes a misunderstood problem. However, the common positive Deltaalpha concept remains empirical. The objective of this study is to investigate the Deltaalpha dependence of residual stress profiles in veneering ceramic layered on Y-TZP frameworks. METHODS: The stress profile was measured with the hole-drilling method in bilayered disc samples of 20mm diameter with a 0.7mm thick Y-TZP framework and a 1.5mm thick veneer layer. 3 commercial and 4 experimental veneering ceramics (n=3 per group) were used to obtain different Deltaalpha varying from -1.3ppm/ degrees C to +3.2ppm/ degrees C, which were determined by dilatometric analyses. RESULTS: Veneer fractures were observed in samples with Deltaalpha>/=+2.3 or </=-0.3ppm/ degrees C. Residual stress profiles measured in other groups showed compressive stresses in the surface, these stresses decreasing with depth and then becoming more compressive again near the interface. Small Deltaalpha variations were shown to induce significant changes in residual stress profiles. Compressive stress near the framework was found to decrease inversely to Deltaalpha. SIGNIFICANCE: Veneer CTE close to Y-TZP (+0.2ppm/ degrees C Deltaalpha) gived the most favorable stress profile. Yet, near the framework, Deltaalpha-induced residual stress varied inversely to predictions. This could be explained by the hypothesis of structural changes occurrence within the Y-TZP surface. Consequently, the optimum Deltaalpha value cannot be determined before understanding Y-TZP's particular behavior when veneered.
Research center :
d‐BRU - Dental Biomaterials Research Unit - ULiège [BE]
Disciplines :
Materials science & engineering Dentistry & oral medicine
Author, co-author :
Mainjot, Amélie ; Université de Liège > Département de sciences dentaires > Biomatériaux dentaires
Najjar, Achref
Jakubowicz-Kohen, Boris D.
Sadoun, Michael J.
Language :
English
Title :
Influence of thermal expansion mismatch on residual stress profile in veneering ceramic layered on zirconia: Measurement by hole-drilling.
Publication date :
September 2015
Journal title :
Dental Materials
ISSN :
0109-5641
eISSN :
1879-0097
Publisher :
Elsevier
Volume :
31
Issue :
9
Pages :
1142–1149
Peer reviewed :
Peer Reviewed verified by ORBi
Commentary :
Copyright (c) 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
S.D. Heintze, and V. Rousson Survival of zirconia- and metal-supported fixed dental prostheses: a systematic review Int J Prosthodont 23 November-December (6) 2010 493 502
J. Pelaez, P.G. Cogolludo, B. Serrano, J.F. Serrano, and M.J. Suarez A four-year prospective clinical evaluation of zirconia and metal-ceramic posterior fixed dental prostheses Int J Prosthodont 25 September-October (5) 2012 451 458
P. Vigolo, and S. Mutinelli Evaluation of zirconium-oxide-based ceramic single-unit posterior fixed dental prostheses (FDPs) generated with two CAD/CAM systems compared to porcelain-fused-to-metal single-unit posterior FDPs: a 5-year clinical prospective study J Prosthodont 21 June (4) 2012 265 269
K.J. Anusavice, K. Kakar, and N. Ferree Which mechanical and physical testing methods are relevant for predicting the clinical performance of ceramic-based dental prostheses? Clin Oral Implants Res 18 June (Suppl. 3) 2007 218 231
M. Wenzelburger, D. Lopez, and R. Gadow Methods and application of residual stress analysis on thermally sprayed coatings and layer composites Surf Coat Technol 201 October (5) 2006 1995 2001
M.B. Prime Residual stress measurement by successive extension of a slot: the crack compliance method Appl Mech Rev 52 2 1999 75 96
M.B. Prime Measuring residual stress and the resulting stress intensity factor in compact tension specimens Fatigue Fract Eng Mater Struct 22 3 1999 195 204
F. Zarone, S. Russo, and R. Sorrentino From porcelain-fused-to-metal to zirconia: clinical and experimental considerations Dent Mater 27 January (1) 2011 83 96
M.V. Swain Unstable cracking (chipping) of veneering porcelain on all-ceramic dental crowns and fixed partial dentures Acta Biomater 5 June (5) 2009 1668 1677
A.K. Mainjot, G.S. Schajer, A.J. Vanheusden, and M.J. Sadoun Influence of cooling rate on residual stress profile in veneering ceramic: measurement by hole-drilling Dent Mater 27 September (9) 2011 906 914
J.P. Coffey, K.J. Anusavice, P.H. DeHoff, R.B. Lee, and B. Hojjatie Influence of contraction mismatch and cooling rate on flexural failure of PFM systems J Dent Res 67 January (1) 1988 61 65
J.S. Shell, and J.P. Nielsen Study of the bond between gold alloys and porcelain J Dent Res 41 November-December 1962 1424 1437
P.H. DeHoff, and K.J. Anusavice Viscoelastic stress analysis of thermally compatible and incompatible metal-ceramic systems Dent Mater 14 July (4) 1998 237 245
I. Denry, and J.R. Kelly State of the art of zirconia for dental applications Dent Mater 24 March (3) 2008 299 307
G. Gostemeyer, M. Jendras, L. Borchers, F.W. Bach, M. Stiesch, P. Kohorst, and et al. Effect of thermal expansion mismatch on the Y-TZP/veneer interfacial adhesion determined by strain energy release rate Influence of cooling rate on zirconia/veneer interfacial adhesion J Prosthodont Res 6 November-December (12) 2011 4532 4538
J. Fischer, B. Stawarczyk, M. Tomic, J.R. Strub, and C.H. Hammerle Effect of thermal misfit between different veneering ceramics and zirconia frameworks on in vitro fracture load of single crowns Dent Mater J 26 November (6) 2007 766 772
J. Fischer, B. Stawarzcyk, A. Trottmann, and C.H. Hammerle Impact of thermal misfit on shear strength of veneering ceramic/zirconia composites Dent Mater 25 April (4) 2009 419 423
M.N. Aboushelib, A.J. Feilzer, N. de Jager, and C.J. Kleverlaan Prestresses in bilayered all-ceramic restorations J Biomed Mater Res B Appl Biomater 87 October (1) 2008 139 145
R. Belli, S. Monteiro Jr., L.N. Baratieri, H. Katte, A. Petschelt, and U. Lohbauer A photoelastic assessment of residual stresses in zirconia-veneer crowns J Dent Res 91 March (3) 2012 316 320
A.K. Mainjot, G.S. Schajer, A.J. Vanheusden, and M.J. Sadoun Residual stress measurement in veneering ceramic by hole-drilling Dent Mater 27 May (5) 2011 439 444
ASTM. Determining residual stresses by the hole-drilling strain-gage method. Standard Test Method E837-08 West Conshohocken. PA, USA: American Society for Testing and Materials; 2008.
G.S. Schajer, and M.B. Prime Use of inverse solutions for residual stress measurements J Eng Mater Technol Trans ASME 128 3 2006 375 382
A.K. Mainjot, G.S. Schajer, A.J. Vanheusden, and M.J. Sadoun Influence of zirconia framework thickness on residual stress profile in veneering ceramic: measurement by hole-drilling Dent Mater 28 April (4) 2012 378 384
A.K. Mainjot, G.S. Schajer, A.J. Vanheusden, and M.J. Sadoun Influence of veneer thickness on residual stress profile in veneering ceramic: measurement by hole-drilling Dent Mater 28 February (2) 2012 160 167
C.H. Hsueh, G.A. Thompson, O.M. Jadaan, A.A. Wereszczak, and P.F. Becher Analyses of layer-thickness effects in bilayered dental ceramics subjected to thermal stresses and ring-on-ring tests Dent Mater 24 January (1) 2008 9 17
G. Gostemeyer, M. Jendras, M.P. Dittmer, F.W. Bach, M. Stiesch, and P. Kohorst Influence of cooling rate on zirconia/veneer interfacial adhesion Acta Biomater 6 December (12) 2010 4532 4538
P.H. DeHoff, K.J. Anusavice, and S.B. Vontivillu Analysis of tempering stresses in metal-ceramic disks J Dent Res 75 February (2) 1996 743 751
K.A. Fukushima, M.J. Sadoun, P.F. Cesar, and A.K. Mainjot Residual stress profiles in veneering ceramic on Y-TZP, alumina and ZTA frameworks: measurement by hole-drilling Dent Mater. 30 February (2) 2014 105 111
A.K. Mainjot, T. Douillard, L. Gremillard, M.J. Sadoun, and J. Chevalier 3D-characterization of the veneer-zirconia interface using FIB nano-tomography Dent Mater 29 February (2) 2013 157 165
B.D. Jakubowicz-Kohen, M.J. Sadoun, T. Douillard, and A.K. Mainjot Influence of firing time and framework thickness on veneered Y-TZP discs curvature Dent Mater 30 February (2) 2014 242 248
J.C. Durand, B. Jacquot, H. Salehi, M. Fages, J. Margerit, and F.J. Cuisinier Confocal Raman microscopic analysis of the zirconia/feldspathic ceramic interface Dent Mater 28 June (6) 2012 661 671
J.C. Durand, B. Jacquot, H. Salehi, J. Margerit, and F.J. Cuisinier Confocal Raman microscopy and SEM/EDS investigations of the interface between the zirconia core and veneering ceramic: the influence of a liner and regeneration firing J Mater Sci Mater Med 23 June (6) 2012 1343 1353
C.M. Ramos, P.F. Cesar, R.F. Lia Mondelli, A.S. Tabata, J. de Souza Santos, and A.F. Sanches Borges Bond strength and Raman analysis of the zirconia-feldspathic porcelain interface J Prosthet Dent 112 October (4) 2014 886 894
M.J. Tholey, C. Berthold, M.V. Swain, and N. Thiel XRD2 micro-diffraction analysis of the interface between Y-TZP and veneering porcelain: role of application methods Dent Mater 26 June (6) 2010 545 552
M.J. Tholey, M.V. Swain, and N. Thiel SEM observations of porcelain Y-TZP interface Dent Mater 25 July (7) 2009 857 862
L. Hallmann, P. Ulmer, S. Wille, and M. Kern Effect of differences in coefficient of thermal expansion of veneer and Y-TZP ceramics on interface phase transformation J Prosthet Dent 112 September (3) 2014 591 599
R. Belli, R. Frankenberger, A. Appelt, J. Schmitt, L.N. Baratieri, P. Greil, and et al. Thermal-induced residual stresses affect the lifetime of zirconia-veneer crowns Dent Mater 29 February (2) 2013 181 190