Influence of zirconia framework thickness on residual stress profile in veneering ceramic: Measurement by hole-drilling.
English
MAINJOT, Amélie mailto [Centre Hospitalier Universitaire de Liège - CHU > > Institut de dentisterie - prothèse fixée]
Schajer, G. S. [> > > >]
Vanheusden, Alain mailto [Université de Liège - ULg > Département de science dentaire > Prothèse dentaire fixe - Anatomie bucco-dentaire]
Sadoun, M. J. [> > > >]
2011
Dental Materials
Elsevier Science
Yes (verified by ORBi)
International
0109-5641
Kidlington
United Kingdom
[en] OBJECTIVES: Framework design is reported to influence chipping in zirconia-based restorations, which is an important cause of failure of such restorations. Residual stress profile in the veneering ceramic after the manufacturing process is an important predictive factor of the mechanical behavior of the material. The objective of this study is to investigate the influence of framework thickness on the stress profile measured in zirconia-based structures. METHODS: The stress profile was measured with the hole-drilling method in bilayered disc samples of 20mm diameter with a 1.5mm thick veneering ceramic layer. Six different framework thicknesses from 0.5mm to 3mm were studied. Two different cooling procedures were also investigated. RESULTS: Compressive stresses were observed in the surface, and tensile stresses in the depth of most of the samples. The slow cooling procedure was found to promote the development of interior tensile stresses, except for the sample with a 3mm thick framework. With the tempering procedure, samples with a 1.5mm thick framework exhibited the most favorable stress profile, while thicker and thinner frameworks exhibited respectively in surface or interior tensile stresses. Significance: The measurements performed highlight the importance of framework thickness, which determine the nature of stresses and can explain clinical failures encountered, especially with thin frameworks. The adequate ratio between veneering ceramic and zirconia is hard to define, restricting the range of indications of zirconia-based restorations until a better understanding of such a delicate veneering process is achieved.
http://hdl.handle.net/2268/109273
10.1016/j.dental.2011.11.009
Copyright (c) 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

File(s) associated to this reference

Fulltext file(s):

FileCommentaryVersionSizeAccess
Restricted access
Mainjot4 orbi.pdfPublisher postprint770.6 kBRequest copy

Bookmark and Share SFX Query

All documents in ORBi are protected by a user license.